S-Plastics Valox EXVX1314 resin is a 20% glass reinforced super high flow nucleated PBT/ASA blend with excellent mechanical properties, high
dimensional stability. Applications: connectors and automotive industry.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 103 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 103 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.7 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 150 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*3 +23°C | 44 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 40 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 165 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 167 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.38 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.76 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.27 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 26 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 250°C, 1500 sec-1 | 173 | Pa-s | ISO 11443 |
| Source GMD, last updated:12/16/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 245 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 40 - 100 | °C |
| Source GMD, last updated:12/16/2008 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox EXVX1314.pdf |
|