S-Plastics Valox HX312C resin is Unreinforced PBT with release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 51 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 30 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 25 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2500 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 30 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 25 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2400 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 53 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 40 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 3 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 2 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 175 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 54 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 |
| CTE, 23°C to 80°C, flow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 175 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 165 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 58 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.9 - 1.6 | % | S-Plastics Method |
| Melt Flow Rate, 250°C/1.2 kgf | 35 | g/10 min | ASTM D 1238 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.35 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.08 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/1.2 kg | 31 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:10/03/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 245 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 40 - 100 | °C |
| Source GMD, last updated:10/03/2007 | ||
|