S-Plastics Valox V3100HR resin isHydrolytically resistant low viscosity polyester grade.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 55 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 50 | % | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 86 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2410 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 52 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 148 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 95°C, flow | 1.19E-04 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Specific Volume | 0.1 | cm³/g | ASTM D 792 |
| Water Absorption, 24 hours | 0.06 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 2.1 - 2.3 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 2.2 - 2.4 | % | S-Plastics Method |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 2.5E+16 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 3.2 mm | 16.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 50/60 Hz | 2.9 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 2.88 | - | ASTM D 150 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.016 | - | ASTM D 150 |
| Source GMD, last updated:02/11/2002 | |||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox V3100HR.pdf |
|