S-Plastics Valox V3900WX resin is PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 48 | MPa | S-Plastics - Japan Method |
| Tensile Stress, yld, Type I, 50 mm/min | 53 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 43 | MPa | ASTM D 638 |
| Tensile Strain, break | 250 | % | S-Plastics - Japan Method |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 50 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2200 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 80 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2200 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 51 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 42 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2090 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 73 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2130 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 800 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 110 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 50 | J | ASTM D 3763 |
| Instrumented Impact Total Energy, -40°C | 50 | J | ASTM D 3673 |
| Izod Impact, notched 80*10*4 +23°C | 41 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 52 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 105 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 75 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 119 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 96 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.84E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 8.97E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 8.84E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.97E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 121 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 123 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 77 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 120 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 120 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.3 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.7 - 1 | % | S-Plastics Method |
| Melt Flow Rate, 265°C/2.16kg | 11 | g/10 min | ASTM D 1238 |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.03 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 9 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL Recognized, 94-5VA Rating (3) | 3 | mm | UL 94 |
| UV-light, water exposure/immersion | F11 | - | UL 746C |
| Source GMD, last updated:10/20/2006 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 265 | °C |
| Nozzle Temperature | 245 - 260 | °C |
| Front - Zone 3 Temperature | 250 - 265 | °C |
| Middle - Zone 2 Temperature | 245 - 260 | °C |
| Rear - Zone 1 Temperature | 240 - 255 | °C |
| Mold Temperature | 65 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.025 - 0.038 | mm |
| Source GMD, last updated:10/20/2006 | ||
Hot-sale product(in stock)
PBT: 325,325FC,310,310SE0
PC+PBT: 357 357U,5220U,V3900WX
PBT + glass filled: DR51, DR48, 420 420se0, 553, 508, 420HP
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
S-Plastics Valox V3900WX.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|