S-Plastics Valox V4860HR resin is 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 116 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 114 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.2 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 9750 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 174 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 2 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6740 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 111 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 110 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.1 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9440 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 183 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 182 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 2.9 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 7870 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 74 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 13 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 176 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 197 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 221 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 205 | °C | ASTM D 648 |
| CTE, -40°C to 95°C, flow | 2.35E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 95°C, xflow | 1.14E-04 | 1/°C | ASTM E 831 |
| CTE, 23°C to 80°C, flow | 2.28E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 1.19E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, approximate maximum | 75 | °C | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 176 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 175 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 188 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.64 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.18 - 0.21 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.75 - 0.94 | % | S-Plastics Method |
| Melt Flow Rate, 250°C/5.0 kgf | 17.8 | g/10 min | ASTM D 1238 |
| Density | 1.64 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.19 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 0.8 | mm | UL 94 by GE |
| Source GMD, last updated:02/02/2005 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 12 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 230 - 260 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 240 - 260 | °C |
| Middle - Zone 2 Temperature | 230 - 250 | °C |
| Rear - Zone 1 Temperature | 220 - 240 | °C |
| Mold Temperature | 60 - 120 | °C |
| Back Pressure | 5 - 10 | MPa |
| Screw Speed | 20 - 100 | rpm |
| Shot to Cylinder Size | 30 - 70 | % |
| Vent Depth | 0.025 - 0.038 | mm |
| Source GMD, last updated:02/02/2005 | ||
Hot-sale product(in stock)
PBT: 325,325FC,310,310SE0
PC+PBT: 357 357U,5220U,V3900WX
PBT + glass filled: DR51, DR48, 420 420se0, 553, 508, 420HP
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
S-Plastics Valox V4860HR.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|