S-Plastics Valox V8060RE resin is 30% glass reinforced PBT+PET blend with 25% post-consumer recycle. Hydrolitically stable. Auto specs for GM, Ford, Chrysler.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 106 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 106 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.8 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.8 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 7230 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 169 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7060 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 747 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 6 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 190 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 207 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 171 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 2.88E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 6.84E-05 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.53 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.25 - 0.55 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.55 - 0.85 | % | S-Plastics Method |
| Melt Flow Rate, 266°C/5.0 kgf | 32 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.6E+16 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in oil, 3.2 mm | 15.7 | kV/mm | ASTM D 149 |
| Relative Permittivity, 100 Hz | 3.4 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.3 | - | ASTM D 150 |
| Dissipation Factor, 100 Hz | 0.0026 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.0155 | - | ASTM D 150 |
| AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 98 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.8 | % | ASTM D 638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7630 | MPa | ASTM D 790 |
| Instrumented Impact, Total Energy, 23°C | 6 | J | ASTM D 3763 |
| AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 107 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D 638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7940 | MPa | ASTM D 790 |
| Instrumented Impact, Total Energy, 23°C | 5 | J | ASTM D 3763 |
|
For more information please download the datasheet |
|
 |
S-Plastics Valox V8060RE.pdf |
|