S-Plastics Valox V9235 resin is Valox heat stabilized, Glass filled grade with mold release based on recycle PET. This grade is typically applied for business Machines applications
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 95 | MPa | ASTM D 638 |
| Tensile Stress, break | 95 | MPa | ASTM D 638 |
| Tensile Strain, yield | 1.8 | % | ASTM D 638 |
| Tensile Strain, break | 1.8 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 6250 | MPa | ASTM D 638 |
| Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 50 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 50 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 19 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 19 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 3.1E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 9.4E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 230 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 230 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.32 - 0.4 | % | S-Plastics Method |
| Density | 1.46 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.36 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.13 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 38 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:08/10/2005 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 130 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 270 - 290 | °C |
| Nozzle Temperature | 260 - 280 | °C |
| Front - Zone 3 Temperature | 270 - 290 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 35 - 65 | °C |
| Source GMD, last updated:08/10/2005 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Valox V9235.pdf |
|