S-Plastics Cycoloy CE8510 resin is Extrusion grade PC/ABS. Low viscosity, high impact and ductility.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 57 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 56 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 125 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2170 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 85 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2350 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 50 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >50 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2250 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 650 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 530 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 60 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*3 +23°C | 50 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 35 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 50 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 35 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 118 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 124 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 107 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 118 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 122 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 120 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.14 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 260°C/5.0 kgf | 8.5 | g/10 min | ASTM D 1238 |
| Density | 1.14 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.1 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.1 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/5.0 kg | 10 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:09/03/2004 | |||
| Parameter | ||
| Film Extrusion | Value | Unit |
| Drying Temperature | 90 - 110 | °C |
| Drying Time | 4 | hrs |
| Drying Time (Cumulative) | 6 - 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Barrell Temperature - Rear | 220 - 250 | °C |
| Barrell Temperature - Middle | 220 - 250 | °C |
| Barrell Temperature - Front | 220 - 250 | °C |
| Die Temperature | 220 - 250 | °C |
| Roll Temperature | 200 - 250 | °C |
| Source GMD, last updated:09/03/2004 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics cycoloy CE8510.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|