S-Plastics Valox 861resin is 30% glass reinforced PBT+PET blend. Color stable, FR. Housewares, appliances; iron skirt, oven trim/panels.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 108 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 110 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.1 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 6200 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 155 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 8270 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 534 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 80 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 212 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 187 | °C | ASTM D 648 |
| Relative Temp Index, Elec | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.73 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.3 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 266°C/5.0 kgf | 45 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 0.76 | mm | UL 94 |
| UL Recognized, 94-5VA Rating (3) | 2.99 | mm | UL 94 |
| Source GMD, last updated:06/05/1998 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 60 - 75 | °C |
| Drying Time | 4 - 5 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Minimum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 275 | °C |
| Nozzle Temperature | 255 - 270 | °C |
| Front - Zone 3 Temperature | 255 - 265 | °C |
| Middle - Zone 2 Temperature | 250 - 260 | °C |
| Rear - Zone 1 Temperature | 245 - 255 | °C |
| Mold Temperature | 65 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.025 - 0.038 | mm |
| Source GMD, last updated:06/05/1998 | ||
Other related products we recommend:
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Valox 861.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|