S-Plastics Valox VR950G30 resin is Industrial Quality Material based, 30% Filler Reinforced, Flame retardant PBT+PET+PC blend
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 115 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 115 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.7 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8500 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 180 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 30 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/120 | 175 | °C | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) (5) | 0.3 - 0.9 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) (5) | 0.5 - 1.2 | % | S-Plastics Method |
| Density | 1.7 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.3 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/2.16 kg | 10 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 21 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 750°C, passes at | 3 | mm | IEC 60695-2-12 |
| Source GMD, last updated:2009/10/12 | |||
| Injection Molding | Value | Unit | |
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 4 - 6 | hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260 - 285 | °C | |
| Nozzle Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 260 - 280 | °C | |
| Middle - Zone 2 Temperature | 255 - 280 | °C | |
| Rear - Zone 1 Temperature | 240 - 260 | °C | |
| Hopper Temperature | 40 - 60 | °C | |
| Mold Temperature | 60 - 110 | °C | |
| Source GMD, last updated:2009/10/12 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
| (5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. |
|||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Valox VR950G30.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|