S-Plastics Cycoloy CY6120 resin is Non-chlorinated and non-brominated flame retardant PC/ABS featuring good flow and impact properties. UL-94 V0 listed at 1.2mm intended for various thin wall applications.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 59 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2960 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 102 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2820 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 58 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 49 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2600 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 93 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 587 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 54 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 96 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 93 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 85 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.38E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 8.46E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C to 80°C, flow | 8.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 8.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 95 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 98 | °C | ISO 306 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.3 - 0.5 | % | S-Plastics Method |
| Melt Flow Rate, 260°C/2.16 kgf | 18 | g/10 min | ASTM D 1238 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 16 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 2.7 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.6 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.0041 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.0086 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.19 | mm | UL 94 |
| Source GMD, last updated:04/11/2002 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 245 - 275 | °C |
| Nozzle Temperature | 245 - 275 | °C |
| Front - Zone 3 Temperature | 245 - 275 | °C |
| Middle - Zone 2 Temperature | 220 - 265 | °C |
| Rear - Zone 1 Temperature | 220 - 255 | °C |
| Mold Temperature | 60 - 80 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 30 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Source GMD, last updated:04/11/2002 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics cycoloy CY6120.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|