S-Plastics Valox VX5530 resin is a flame retarded, 15% glass fibre reinforced, 10% mineral filled PBT+PC blend with excellent low warpage
characteristics.
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 75 | mg/1000cy | S-Plastics Method |
| Tensile Stress, break, 5 mm/min | 100 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7500 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 150 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6950 | MPa | ISO 178 |
| Hardness, H358/30 | 160 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 32 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 32 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 4 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 34 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 34 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 3.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 173 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 175 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 137 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 125 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 110 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 125 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.3 - 0.5 | % | S-Plastics Method |
| Density | 1.57 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 30 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, passes at | 2.5 | mm | IEC 60695-2-12 |
| Source GMD, last updated:09/02/1999 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 270 | °C |
| Nozzle Temperature | 240 - 260 | °C |
| Front - Zone 3 Temperature | 245 - 265 | °C |
| Middle - Zone 2 Temperature | 240 - 255 | °C |
| Rear - Zone 1 Temperature | 230 - 245 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 40 - 100 | °C |
| Source GMD, last updated:09/02/1999 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
SS-Plastics Valox VX5530.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|