S-Plastics Valox EXVX1113resin is a 40% Glass / Mica reinforced polyethylene terephtalate with low warpage, higher strength and improved electricalproperties.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 120 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 12500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 195 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 11500 | MPa | ISO 178 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 236 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.2 - 0.4 | % | S-Plastics Method |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+16 | Ohm-cm | IEC 60093 |
| Dielectric Strength, in oil, 3.2 mm | 19 | kV/mm | IEC 60243-1 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 0.8 | mm | UL 94 by GE |
| Source GMD, last updated:12/13/2002 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 - 130 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 270 - 290 | °C |
| Nozzle Temperature | 260 - 280 | °C |
| Front - Zone 3 Temperature | 270 - 290 | °C |
| Middle - Zone 2 Temperature | 260 - 280 | °C |
| Rear - Zone 1 Temperature | 250 - 270 | °C |
| Hopper Temperature | 40 - 60 | °C |
| Mold Temperature | 90 - 120 | °C |
| Source GMD, last updated:12/13/2002 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Valox EXVX1113.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|