S-Plastics Cycolac EXABS01 resin isSheet extrusion ABS with medium impact.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 39 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 28 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.1 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 31.6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2030 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 63 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2100 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 411 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 277 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 33 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 93 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 80 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.01E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.04E-04 | 1/°C | ASTM E 831 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.03 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.6 - 0.8 | % | S-Plastics Method |
| Melt Viscosity, 240°C, 100 sec-1 | 14000 | poise | ASTM D 3825 |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 4 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 4 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 1.52 | mm | UL 94 |
| Source GMD, last updated:04/18/2002 | |||
| • Recommend initial lower temperatures settings to avoid material degradation/hang-up in die. | ||
| • Maintain melt temperature within processing range. | ||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 4 - 5 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.02 - 0.04 | % |
| Minimum Moisture Content | 0.04 | % |
| Melt Temperature (Parison) | 215 - 230 | °C |
| Barrel - Zone 1 Temperature | 205 - 225 | °C |
| Barrel - Zone 2 Temperature | 205 - 225 | °C |
| Barrel - Zone 3 Temperature | 205 - 225 | °C |
| Barrel - Zone 4 Temperature | 205 - 225 | °C |
| Adapter - Zone 5 Temperature | 210 - 230 | °C |
| Head - Zone 6 - Top Temperature | 215 - 230 | °C |
| Head - Zone 7 - Bottom Temperature | 215 - 230 | °C |
| Screw Speed | 20 - 60 | rpm |
| Extruder Feed Zone Temperature | 60 - 75 | °C |
| Mold Temperature | 40 - 80 | °C |
| Die Temperature | 215 - 235 | °C |
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
S-Plastics Cycolac EXABS01.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|