S-Plastics Lubricomp QL002 resin is
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 52 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2680 | MPa | ASTM D 638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2270 | MPa | ASTM D 790 |
| Tensile Stress, break, 5 mm/min | 61 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 4.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2480 | MPa | ISO 527 |
| Flexural Stress | 73 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2040 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 399 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 39 | J/m | ASTM D 256 |
| Multiaxial Impact | 0 | J | ISO 6603 |
| Instrumented Impact Total Energy, 23°C | 3 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 164 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 63 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 1.12E+02 | 1/°C | ASTM D 696 |
| CTE, -30°C to 30°C, xflow | 1.15E+02 | 1/°C | ASTM D 696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 143 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 54 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.15 | - | ASTM D 792 |
| Density | 1.14 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.26 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs (5) | 0.9 - 3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs (5) | 1 - 4 | % | ASTM D 955 |
| Wear Factor Washer | 35 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Wear Factor Ring | 0 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.38 | - | ASTM D 3702 Modified |
| Static COF | 0.25 | - | ASTM D 3702 Modified |
| Moisture Absorption (23°C / 50% RH) | 0.38 | % | ISO 62 |
| Source GMD, last updated:2009/07/28 | |||
Processing
| Parameter | |||
| Injection Molding | Value | Unit | |
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | hrs | |
| Maximum Moisture Content | 0.12 - 0.2 | % | |
| Melt Temperature | 270 - 275 | °C | |
| Front - Zone 3 Temperature | 270 - 280 | °C | |
| Middle - Zone 2 Temperature | 260 - 270 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Source GMD, last updated:2009/07/28 | |||
In recent years, we have deeply cultivated the domestic market and actively explored foreign markets.Up to now, we have provided high-quality products and services to more than 1,000 customers in various industries, including: electronics and electrical appliances, medical, food, automotive electronics, optoelectronic communications, photovoltaic new energy, water treatment, transportation and other industries.
Samtion chemical supplies engineering plastics and special modified materials of S-Plastics and other brands.Our authentic products are guaranteed, with complete qualifications and superior supply capacity and price advantages.
Every batch of our products is subject to strict quality inspection to ensure the original supply. All products have MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA certificates!!
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Lubricomp QL002.pdf |
|