S-Plastics Cycoloy EXCY0052 resin is Heat Stabilized, Impact Modified, PC+ABS, for SLX films Tie layer
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 52 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 56 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.9 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 125 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2170 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 85 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2350 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 650 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 122 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 103 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.14 | - | ASTM D 792 |
| Melt Flow Rate, 260°C/5.0 kgf | 8.1 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:03/23/2004 | |||
| Parameter | ||
| Film Extrusion | Value | Unit |
| Drying Temperature | 90 - 110 | °C |
| Drying Time | 4 | hrs |
| Drying Time (Cumulative) | 6 - 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Barrell Temperature - Rear | 220 - 250 | °C |
| Barrell Temperature - Middle | 220 - 250 | °C |
| Barrell Temperature - Front | 220 - 250 | °C |
| Die Temperature | 220 - 250 | °C |
| Roll Temperature | 200 - 250 | °C |
| Source GMD, last updated:03/23/2004 | ||
|
For more information please download the datasheet |
|
 |