S-Plastics Cycolac REC550HF resin is ABS, High Flow, Rework Molding Grade
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 34 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 20 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 68 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2450 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 80 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate, 220°C/10.0 kg | 35 | g/10 min | ISO 1133 |
| Source GMD, last updated:2009/10/22 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 2 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.01 | % |
| Melt Temperature | 205 - 245 | °C |
| Nozzle Temperature | 205 - 245 | °C |
| Front - Zone 3 Temperature | 205 - 225 | °C |
| Middle - Zone 2 Temperature | 200 - 210 | °C |
| Rear - Zone 1 Temperature | 190 - 200 | °C |
| Mold Temperature | 50 - 70 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Shot to Cylinder Size | 50 - 70 | % |
| Vent Depth | 0.038 - 0.051 | mm |
| Source GMD, last updated:2009/10/22 | ||
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
S-Plastics Cycolac REC550HF.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|