S-Plastics Cycolac GPX3800UV resin is High impact, uv stabilised, extrusion grade of ABS
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 37 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 29 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2130 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 62 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1940 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 448 | J/m | ASTM D 256 |
| Izod Impact, notched, -40°C | 240 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 78 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 82 | °C | ASTM D 648 |
| CTE, -40°C to 60°C, flow | 1.65E-04 | 1/°C | ASTM E 831 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.03 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.8 | % | S-Plastics Method |
| Melt Flow Rate, 230°C/5 kgf | 3 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:06/18/1999 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 2 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Melt Temperature | 205 - 220 | °C |
| Source GMD, last updated:06/18/1999 | ||
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
S-Plastics Cycolac GPX3800UV.pdf |
|