S-Plastics Lubricomp RFL36S resin is
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 139 | MPa | ASTM D 638 |
| Tensile Strain, break | 2.1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11230 | MPa | ASTM D 638 |
| Flexural Stress | 236 | MPa | ASTM D 790 |
| Flexural Modulus | 9740 | MPa | ASTM D 790 |
| Tensile Stress, break | 138 | MPa | ISO 527 |
| Tensile Strain, break | 2.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9800 | MPa | ISO 527 |
| Flexural Stress | 211 | MPa | ISO 178 |
| Flexural Modulus | 9700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 907 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 106 | J/m | ASTM D 256 |
| Izod Impact, notched, -40°C | 386 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 10 | J | ASTM D 3763 |
| Multiaxial Impact | 2 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 51 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 248 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 3.79E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 3.78E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.5E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 248 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.51 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.62 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.3 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.1 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.32 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.15 | % | ISO 294 |
| Wear Factor Washer | 12 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.58 | - | ASTM D 3702 Modified |
| Dynamic COF | 0.59 | - | ASTM D 3702 Modified |
| Static COF | 0.49 | - | ASTM D 3702 Modified |
| Static COF | 0.46 | - | ASTM D 3702 Modified |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Source GMD, last updated:09/30/2004 | |||
Processing
| Parameter | |||
| Injection Molding | Value | Unit | |
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm | |
| Source GMD, last updated:09/30/2004 | |||
In recent years, we have deeply cultivated the domestic market and actively explored foreign markets.Up to now, we have provided high-quality products and services to more than 1,000 customers in various industries, including: electronics and electrical appliances, medical, food, automotive electronics, optoelectronic communications, photovoltaic new energy, water treatment, transportation and other industries.
Samtion chemical supplies engineering plastics and special modified materials of S-Plastics and other brands.Our authentic products are guaranteed, with complete qualifications and superior supply capacity and price advantages.
Every batch of our products is subject to strict quality inspection to ensure the original supply. All products have MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA certificates!!
|
For more information please download the datesheet |
|
 |
S-Plastics Lubricomp RFL36S.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|