S-Plastics Cycoloy EXCY0102 resin is Modified PC blend offering metallic look with minimal flowline visibility.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 61 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 59 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | >90 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2400 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 61 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 59 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 100 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 70 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 37 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 134 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 106 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 7.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.22 | W/m-°C | ASTM E 1530 |
| CTE, -40°C to 40°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 134 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 136 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 106 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.16 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 260°C/5.0 kgf | 14 | g/10 min | ASTM D 1238 |
| Density | 1.16 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.6 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 11 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Dielectric Strength, in oil, 1.6 mm | 26 | kV/mm | ASTM D 149 |
| Relative Permittivity, 1 MHz | 2.8 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.007 | - | ASTM D 150 |
| Source GMD, last updated:03/09/2005 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 300 - 320 | °C |
| Nozzle Temperature | 300 - 320 | °C |
| Front - Zone 3 Temperature | 300 - 320 | °C |
| Middle - Zone 2 Temperature | 285 - 305 | °C |
| Rear - Zone 1 Temperature | 270 - 290 | °C |
| Mold Temperature | 80 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 80 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:03/09/2005 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics cycoloy EXCY0102.pdf |
|