S-Plastics Cycoloy EXCY0136 resin is an injection moldable PC/ABS blend with non-brominated and non-chlorinated flame retardant systems. Thin wall FR tog with excellent impact/flow balance makes it ideal for enclosures in medical and other applications.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 65 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 58 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.1 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 100 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2950 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 104 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2750 | MPa | ASTM D 790 |
| Tensile Stress, yield, 50 mm/min | 65 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 40 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 90 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2950 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 96 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 700 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 175 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 65 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 22 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 106 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 100 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 89 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 99 | °C | ASTM D 648 |
| Ball Pressure Test, 75°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 106 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 107 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 93 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.19 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Melt Flow Rate, 260°C/2.16 kgf | 21 | g/10 min | ASTM D 1238 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 22 | cm³/10 min | ISO 1133 |
| Melt Viscosity, 260°C, 1500 sec-1 | 200 | Pa-s | ISO 11443 |
| ELECTRICAL | Value | Unit | Standard |
| Hot Wire Ignition {PLC) | 3 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-1 Flame Class Rating (3)(4) | 0.6 | mm | UL 94 by GE |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 0.75 | mm | UL 94 by GE |
| UL Compliant, 94-5VB Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Glow Wire Flammability Index 960°C, passes at | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Source GMD, last updated:11/09/2005 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 270 - 300 | °C |
| Nozzle Temperature | 265 - 300 | °C |
| Front - Zone 3 Temperature | 265 - 300 | °C |
| Middle - Zone 2 Temperature | 260 - 300 | °C |
| Rear - Zone 1 Temperature | 260 - 300 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 90 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 80 | % |
| Vent Depth | 0.038 - 0.076 | mm |
| Source GMD, last updated:11/09/2005 | ||
|
For more information please download the datasheet |
|
 |