S-Plastics Cycoloy EXCY0197 resin
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 64 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 85 | % | ASTM D 638 |
| Tensile Stress, yield, 50 mm/min | 66 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 67 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | >100 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | >100 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2420 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 96 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2470 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 795 | J/m | ASTM D 256 |
| Izod Impact, notched, 0°C | 525 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 215 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*3 +23°C | 52 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 0°C | 14 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 12 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 +23°C | 13 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 0°C | 14 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 12 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 28 | kJ/m² | ISO 179/1eA |
| Charpy 0°C, V-notch Edgew 80*10*3 sp=62mm | 12 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 17 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 118 | °C | ASTM D 648 |
| Ball Pressure Test, 125°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/120 | 134 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 116 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.18 | - | ASTM D 792 |
| Melt Flow Rate, 250°C/5.0 kgf | 15.5 | g/10 min | ASTM D 1238 |
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 5 | cm³/10 min | ISO 1133 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 13 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-1 Flame Class Rating (3)(4) | 1.2 | mm | UL 94 by GE |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.5 | mm | UL 94 by GE |
| Source GMD, last updated:12/04/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 90 - 100 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 250 - 300 | °C |
| Nozzle Temperature | 230 - 290 | °C |
| Front - Zone 3 Temperature | 240 - 300 | °C |
| Middle - Zone 2 Temperature | 230 - 290 | °C |
| Rear - Zone 1 Temperature | 210 - 260 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 60 - 90 | °C |
| Source GMD, last updated:12/04/2007 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics cycoloy EXCY0197.pdf |
|