S-Plastics Cycolac INP581 resin is High flow, low molecular weight SAN. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direct weather exposure. Provides excellent flow for demanding injection molding applications.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 48 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 60 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4080 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 66 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3440 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 122 | - | ASTM D 785 |
| Flexural Stress, yield, 2 mm/min | 36 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3520 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 23 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 12 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 1 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 1 | kJ/m² | ISO 180/1A |
| Charpy Impact, notched, 23°C | 1 | kJ/m² | ISO 179/2C |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 97 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 86 | °C | ASTM D 648 |
| Vicat Softening Temp, Rate B/50 | 102 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 104 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 82 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.08 | - | ASTM D 792 |
| Melt Flow Rate, 230°C/3.8 kgf | 37.7 | g/10 min | ASTM D 1238 |
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Flow Rate, 220°C/10.0 kg | 98 | g/10 min | ISO 1133 |
| OPTICAL | Value | Unit | Standard |
| Yellowness Index | 1 | - | ASTM D 1925 |
| Source GMD, last updated:2010/02/25 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours | |||
| storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
| (5) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. |
|||
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
S-Plastics Cycolac INP581.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|