S-Plastics Cycoloy EXCY0259 resin is PC+ABS with High Modulus, Low CTE.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 60 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 59 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 130 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4700 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 106 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 4200 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 59 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 44 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.7 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 91 | % | ISO 527 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 260 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 59 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 124 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 4.3E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 9.E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temp, Rate B/50 | 137 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.27 | - | ASTM D 792 |
| Melt Flow Rate, 260°C/5.0 kgf | 9.4 | g/10 min | ASTM D 1238 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 8 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:07/14/2008 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. | |||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
For more information please download the datasheet | |