S-Plastics Cycoloy EXCY0295 resin is M1/F1 extrusion grade for public transport interior and building & contrsuction
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 66 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 42 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.7 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 20 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 4900 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 112 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 4820 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Multiaxial Impact | 125 | J | ISO 6603 |
| Izod Impact, notched 80*10*3 +23°C | 55 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/120 | 131 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 118 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 5 | cm³/10 min | ISO 1133 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.2 | mm | UL 94 by GE |
| UL Compliant, 94-5VB Rating (3)(4) | 1.2 | mm | UL 94 by GE |
| Source GMD, last updated:2010/08/25 | |||
| Parameter | ||
| Sheet Extrusion | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 250 - 270 | °C |
| Barrel - Zone 1 Temperature | 195 - 205 | °C |
| Barrel - Zone 2 Temperature | 200 - 220 | °C |
| Barrel - Zone 3 Temperature | 220 - 240 | °C |
| Barrel - Zone 4 Temperature | 230 - 260 | °C |
| Adapter Temperature | 230 - 260 | °C |
| Die Temperature | 230 - 245 | °C |
| Roll Stack Temp - Top | 100 - 110 | °C |
| Roll Stack Temp - Middle | 110 - 120 | °C |
| Roll Stack Temp - Bottom | 145 - 155 | °C |
| Source GMD, last updated:2010/08/25 | ||
For more information please download the datasheet | |
 | S-Plastics cycoloy EXCY0295.pdf |
Get The Latest Quotation |