S-Plastics Cycoloy FXC630SP resin is the grade code for the Speckle effect in PC/ABS. Speckle is part of the VisualFX portfolio, and it is offered in a range of colors with a "speckled" appearence. High heat/good flow characteristics. Appliances/Automotive/Telecommunication & Consumer Goods are some of the markets typically using this effect. Color Package may affect performance, Application testing always recommended.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 82 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 5 mm/min | 57 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 44 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 3.7 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 24.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2750 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 98 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2800 | MPa | ISO 178 |
| Hardness, H358/30 | 116 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 122 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*3 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*3 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 8 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.2 | W/m-°C | ISO 8302 |
| CTE, -40°C to 40°C, flow | 7.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Ball Pressure Test, approximate maximum | 85 | °C | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 94 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 97 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 79 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.4 - 0.6 | % | S-Plastics Method |
| Density | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.6 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Melt Volume Rate, MVR at 260°C/2.16 kg | 13 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 35 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 25 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 2.8 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.004 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.008 | - | IEC 60250 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-2 Flame Class Rating (3) | 1 | mm | UL 94 |
| UL Recognized, 94V-1 Flame Class Rating (3) | 1.2 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL Recognized, 94-5VB Rating (3) | 2 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 32 | % | ISO 4589 |
| Source GMD, last updated:11/05/2002 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 - 90 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 230 - 270 | °C |
| Nozzle Temperature | 220 - 260 | °C |
| Front - Zone 3 Temperature | 230 - 270 | °C |
| Middle - Zone 2 Temperature | 220 - 260 | °C |
| Rear - Zone 1 Temperature | 200 - 230 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Mold Temperature | 50 - 70 | °C |
| Source GMD, last updated:11/05/2002 | ||
|