S-Plastics Cycolac LS resin is ABS, extrusion grade. Superior toughness, high gloss, good stress cracking/ chemical resistance and excellent forming characteristics.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 35 | MPa | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1790 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 58 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1790 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 94 | - | ASTM D 785 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 453 | J/m | ASTM D 256 |
| Izod Impact, notched, -40°C | 133 | J/m | ASTM D 256 |
| Falling Dart Impact, 23°C | 40 | J | S-Plastics Method |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 95 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.08E-04 | 1/°C | ASTM E 831 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.02 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.8 | % | S-Plastics Method |
| Melt Flow Rate, 230°C/3.8 kgf | 1 | g/10 min | ASTM D 1238 |
| OPTICAL | Value | Unit | Standard |
| Gloss, untextured, 60 deg (sheet) | 90 | - | ASTM D 523 |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 4 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 1 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 |
| Source GMD, last updated:12/29/1999 | |||
| • Recommend initial lower temperatures settings to avoid material degradation/hang-up in die. | ||
| Parameter | ||
| Sheet Extrusion | Value | Unit |
| Drying Temperature | 80 - 95 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0 - 0.02 | % |
| Melt Temperature | 215 - 260 | °C |
| Barrel - Zone 1 Temperature | 170 - 200 | °C |
| Barrel - Zone 2 Temperature | 180 - 220 | °C |
| Barrel - Zone 3 Temperature | 190 - 225 | °C |
| Barrel - Zone 4 Temperature | 200 - 240 | °C |
| Adapter Temperature | 205 - 250 | °C |
| Die Temperature | 205 - 250 | °C |
| Roll Stack Temp - Top | 90 - 95 | °C |
| Roll Stack Temp - Middle | 95 - 105 | °C |
| Roll Stack Temp - Bottom | 100 - 105 | °C |
| Source GMD, last updated:12/29/1999 | ||
With a strong sales network and strength, we have warehousing services in Guangzhou, Dongguan, Shenzhen free trade zone, Hong Kong and other four places (conventional product inventory exceeds 1000 tons). We can provide customers with rapid response, professional service and excellent products!
|
For more information please download the datasheet |
|
|
S-Plastics Cycolac LS.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|