S-Plastics Ultem 1000E resin is Transparent, standard flow Polyimide (Tg 217C) with internal mold release. ECO Conforming. US FDA and EU Food Contact compliant, NSF 51 Listing. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU1000E.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 110 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3580 | MPa | ASTM D 638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 3510 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 218 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 210 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 201 | °C | ASTM D 648 |
| CTE, -20°C to 150°C, flow | 5.58E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C to 150°C, xflow | 5.4E-05 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.22 | W/m-°C | ASTM C 177 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.27 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.25 | % | ASTM D 570 |
| Water Absorption, equilibrium, 23C | 1.25 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 12 | g/10 min | ASTM D 1238 |
| Poisson's Ratio | 0.3 | - | ASTM D 638 |
| Source GMD, last updated:07/02/2002 | |||
| Parameter | ||
| Extrusion Blow Molding | Value | Unit |
| Drying Temperature | 140 - 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.01 - 0.02 | % |
| Melt Temperature (Parison) | 320 - 355 | °C |
| Barrel - Zone 1 Temperature | 325 - 350 | °C |
| Barrel - Zone 2 Temperature | 330 - 355 | °C |
| Barrel - Zone 3 Temperature | 330 - 355 | °C |
| Barrel - Zone 4 Temperature | 330 - 355 | °C |
| Adapter - Zone 5 Temperature | 330 - 355 | °C |
| Head - Zone 6 - Top Temperature | 330 - 355 | °C |
| Head - Zone 7 - Bottom Temperature | 330 - 355 | °C |
| Screw Speed | 10 - 70 | rpm |
| Mold Temperature | 65 - 175 | °C |
| Die Temperature | 325 - 355 | °C |
| Source GMD, last updated:07/02/2002 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem 1000E.pdf |
|