S-Plastics Verton NV0061EV_GY7E148 resin is Preliminary data for 30% long fiber single pellet non-halogen FR color filled PC/ABS
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 112 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 112 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.3 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 9760 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 142 | MPa | ASTM D 790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 142 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 10200 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 94 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 94 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.1 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9060 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 143 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 143 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 1.6 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 8910 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 329 | J/m | ASTM D 4812 |
| Izod Impact, unnotched, -40°C | 374 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 238 | J/m | ASTM D 256 |
| Izod Impact, notched, -40°C | 184 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 10 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 27 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -40°C | 26 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 21 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 21 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 85 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 2.78E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 6.68E-05 | 1/°C | ASTM E 831 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 87 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.453 | g/cm³ | ASTM D 792 |
| Water Absorption, 24 hours | 0.088 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.08 - 0.28 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.34 - 0.54 | % | ASTM D 955 |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Water Absorption, 23°C/24hrs | 0.09 | % | ISO 62-1 |
| Source GMD, last updated:01/05/2009 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 50 - 60 | °C |
| Drying Time | 2 - 4 | hrs |
| Maximum Moisture Content | 0.04 | % |
| Melt Temperature | 220 - 255 | °C |
| Front - Zone 3 Temperature | 215 - 245 | °C |
| Middle - Zone 2 Temperature | 210 - 245 | °C |
| Rear - Zone 1 Temperature | 205 - 235 | °C |
| Mold Temperature | 35 - 65 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 12 - 40 | rpm |
| Source GMD, last updated:01/05/2009 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |