S-Plastics Verton OV00A resin is a compound based on Polyphenylene Sulfide resin containing Long Glass Fiber.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 124 | MPa | ASTM D 638 |
| Tensile Strain, yield | 1 | % | ASTM D 638 |
| Tensile Strain, break | 1 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 15160 | MPa | ASTM D 638 |
| Flexural Stress | 255 | MPa | ASTM D 790 |
| Flexural Modulus | 17230 | MPa | ASTM D 790 |
| Tensile Stress, break | 190 | MPa | ISO 527 |
| Tensile Strain, break | 1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 20000 | MPa | ISO 527 |
| Flexural Stress | 285 | MPa | ISO 178 |
| Flexural Modulus | 17800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 213 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 31 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 281 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow, 24 hrs | 0.1 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ISO 294 |
| Density | 1.73 | g/cm³ | ISO 1183 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 0.68 | mm | UL 94 by GE |
| Source GMD, last updated:05/12/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.05 | % |
| Melt Temperature | 240 - 265 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 245 - 255 | °C |
| Rear - Zone 1 Temperature | 220 - 230 | °C |
| Mold Temperature | 80 - 100 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:05/12/2007 |
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton OV00A.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|