S-Plastics Verton PV007SV_YW8D151 resin is Preliminary data for 35% long fiber single pellet color filled PA6
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 174 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 9300 | MPa | ASTM D 638 |
| Flexural Stress | 216 | MPa | ASTM D 790 |
| Flexural Modulus | 6420 | MPa | ASTM D 790 |
| Tensile Stress, break | 190 | MPa | ISO 527 |
| Tensile Strain, break | 2.8 | % | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 238 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7700 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1160 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 123 | J/m | ASTM D 256 |
| Izod Impact, notched, -40°C | 191 | J/m | ASTM D 256 |
| Izod Impact, unnotched 80*10*4 +23°C | 70 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 18 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 18 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.4 | g/cm³ | ASTM D 792 |
| Source GMD, last updated:08/12/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 270 - 295 | °C |
| Front - Zone 3 Temperature | 270 - 290 | °C |
| Middle - Zone 2 Temperature | 270 - 290 | °C |
| Rear - Zone 1 Temperature | 260 - 275 | °C |
| Mold Temperature | 85 - 100 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 20 - 60 | rpm |
| Source GMD, last updated:08/12/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton PV007SV_YW8D151.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|