S-Plastics Verton RV008ESV_GY7E072 resin is Preliminary data for 40% long glass fiber filled, single color pellet gray, PA66
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 184 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 182 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.1 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 11560 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 273 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 11300 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 195 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 195 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2.3 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10440 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 276 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10190 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1080 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 246 | J/m | ASTM D 256 |
| Izod Impact, notched, -40°C | 223 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 7 | J | ASTM D 3763 |
| Instrumented Impact Total Energy, 23°C | 16 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 71 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -40°C | 69 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 27 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 259 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 255 | °C | ASTM D 648 |
| CTE, -30°C to 30°C, flow | 2.32E-05 | 1/°C | ASTM E 831 |
| CTE, -30°C to 30°C, xflow | 5.83E-05 | 1/°C | ASTM E 831 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 260 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 256 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.485 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.93 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.23 - 0.43 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.9 - 1.1 | % | ASTM D 955 |
| Density | 1.48 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.65 | % | ISO 62 |
| Source GMD, last updated:10/30/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 290 - 305 | °C |
| Front - Zone 3 Temperature | 290 - 300 | °C |
| Middle - Zone 2 Temperature | 290 - 300 | °C |
| Rear - Zone 1 Temperature | 280 - 295 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/30/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton RV008ESV_GY7E072.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|