S-Plastics Verton RV00AE resin is a compound based on PA 66 rsin containing Long Glass Fiber. Added features include; Easy Molding.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 265 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 18380 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 370 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 15550 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Multiaxial Impact | 152 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 89 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 45 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -40°C | 38 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 1.86E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 6.73E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 258 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 253 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow, 24 hrs | 0.18 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.22 | % | ISO 294 |
| Density | 1.58 | g/cm³ | ISO 1183 |
| Source GMD, last updated:09/26/2008 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 290 - 305 | °C |
| Front - Zone 3 Temperature | 290 - 300 | °C |
| Middle - Zone 2 Temperature | 290 - 300 | °C |
| Rear - Zone 1 Temperature | 280 - 295 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/26/2008 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton RV00AE.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|