S-Plastics Verton RVL28 resin is a compound based on Nylon 66 resin containing Long Glass Fiber, PTFE. Added features of this material include:
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 234 | MPa | ASTM D 638 |
| Tensile Stress, break | 234 | MPa | ASTM D 638 |
| Tensile Strain, yield | 2.3 | % | ASTM D 638 |
| Tensile Strain, break | 2.3 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 14470 | MPa | ASTM D 638 |
| Flexural Stress | 337 | MPa | ASTM D 790 |
| Flexural Modulus | 12410 | MPa | ASTM D 790 |
| Tensile Stress, yield | 228 | MPa | ISO 527 |
| Tensile Stress, break | 228 | MPa | ISO 527 |
| Tensile Strain, yield | 2.4 | % | ISO 527 |
| Tensile Strain, break | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 13230 | MPa | ISO 527 |
| Flexural Stress | 351 | MPa | ISO 178 |
| Flexural Modulus | 13000 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1409 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 256 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 14 | J | ASTM D 3763 |
| Multiaxial Impact | 7 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 93 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 23 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 256 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 253 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 4.86E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 2.16E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 4.9E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 2.1E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 255 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 259 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.58 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.5 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.4 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.33 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.77 | % | ISO 294 |
| Density | 1.57 | g/cm³ | ISO 1183 |
| Source GMD, last updated:08/02/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.15 - 0.25 | % |
| Melt Temperature | 290 - 305 | °C |
| Front - Zone 3 Temperature | 290 - 300 | °C |
| Middle - Zone 2 Temperature | 290 - 300 | °C |
| Rear - Zone 1 Temperature | 280 - 295 | °C |
| Mold Temperature | 95 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:08/02/2007 | ||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
S-Plastics Verton RVL28.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|