S-Plastics Ultem 1010X resin is Enhanced flow Polyimide (Tg 217C) with low ionic contamination of less than 0.1 ppm each of leachable chloride and sulphates.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 110 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3580 | MPa | ASTM D 638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 3510 | MPa | ASTM D 790 |
| Hardness, Rockwell M | 109 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 32 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 218 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 207 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 198 | °C | ASTM D 648 |
| CTE, -20°C to 150°C, flow | 5.58E-05 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.22 | W/m-°C | ASTM C 177 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.27 | - | ASTM D 792 |
| Water Absorption, 24 hours | 0.25 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 17.8 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+17 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 1.6 mm | 32.6 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm | 27.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 1 kHz | 3.15 | - | ASTM D 150 |
| Dissipation Factor, 1 kHz | 0.0013 | - | ASTM D 150 |
| Dissipation Factor, 2450 MHz | 0.0025 | - | ASTM D 150 |
| Source GMD, last updated:04/22/2003 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded |
|||
| samples. All samples tested under ISO test standards are prepared according to ISO 294. | |||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem 1010X.pdf |
|