S-Plastics Stat-kon 9X06519 resin is a compound based on Cyclic Olefinic Copolymer resin containing Carbon Fiber. Added features of this
material include: Clean Compounding System.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 74 | MPa | ASTM D 638 |
| Tensile Strain, break | 0.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 16040 | MPa | ASTM D 638 |
| Flexural Stress | 158 | MPa | ASTM D 790 |
| Flexural Modulus | 16680 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 122 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 32 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 150 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 2.8E-06 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.26E-05 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.17 | g/cm³ | ASTM D 792 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+01 - 1.E+05 | Ohm | ASTM D 257 |
| Source GMD, last updated:02/03/2005 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 260 - 315 | °C |
| Front - Zone 3 Temperature | 300 - 310 | °C |
| Middle - Zone 2 Temperature | 275 - 290 | °C |
| Rear - Zone 1 Temperature | 255 - 265 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:02/03/2005 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon 9X06519.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|