S-Plastics Ultem 1100F resin is Standard flow Polyimide (Tg 217C). ECO Conforming. US FDA and EU Food Contact compliant. Effective June 2007, this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 110 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 70 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3720 | MPa | ASTM D 638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 3720 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3.2 mm | 1548 | J/m | ASTM D 256 |
| Gardner, 23°C | 21 | J | ASTM D 3029 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 198 | °C | ASTM D 648 |
| Relative Temp Index, Elec | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 170 | °C | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.36 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 8.8 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D 495 |
| Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A |
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| Source GMD, last updated:01/11/2000 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 350 - 400 | °C |
| Nozzle Temperature | 345 - 400 | °C |
| Front - Zone 3 Temperature | 345 - 400 | °C |
| Middle - Zone 2 Temperature | 340 - 400 | °C |
| Rear - Zone 1 Temperature | 330 - 400 | °C |
| Mold Temperature | 135 - 165 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:01/11/2000 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem 1100F.pdf |
|