S-Plastics Ultem CRS5211R resin is20% Glass fiber filled, enhanced flow Polyimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 137 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 144 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 6890 | MPa | ASTM D 638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 213 | MPa | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 6890 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 74 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3.2 mm | 459 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 218 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.45 | - | ASTM D 792 |
| Melt Flow Rate, 337°C/6.6 kgf | 5.5 | g/10 min | ASTM D 1238 |
| Source GMD, last updated:01/13/2000 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 365 - 390 | °C |
| Nozzle Temperature | 360 - 380 | °C |
| Front - Zone 3 Temperature | 365 - 390 | °C |
| Middle - Zone 2 Temperature | 355 - 375 | °C |
| Rear - Zone 1 Temperature | 345 - 365 | °C |
| Mold Temperature | 135 - 165 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:01/13/2000 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem CRS5211R.pdf |
|