S-Plastics Stat-kon DD0009 resin is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Powder. Added features of
this material include: Electrically Conductive, Flame Retardant.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 61 | MPa | ASTM D 638 |
| Tensile Stress, break | 53 | MPa | ASTM D 638 |
| Tensile Strain, yield | 1.2 | % | ASTM D 638 |
| Tensile Strain, break | 5.6 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2820 | MPa | ASTM D 638 |
| Flexural Stress | 108 | MPa | ASTM D 790 |
| Flexural Modulus | 2820 | MPa | ASTM D 790 |
| Tensile Stress, yield | 62 | MPa | ISO 527 |
| Tensile Stress, break | 57 | MPa | ISO 527 |
| Tensile Strain, yield | 4.1 | % | ISO 527 |
| Tensile Strain, break | 7.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2810 | MPa | ISO 527 |
| Flexural Stress | 102 | MPa | ISO 178 |
| Flexural Modulus | 2880 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1556 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 68 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 10 | J | ASTM D 3763 |
| Multiaxial Impact | 5 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 70 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 141 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 132 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 5.36E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 5.67E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 5.36E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.67E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 139 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 131 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.32 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.18 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 0.8 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 0.75 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.72 | % | ISO 294 |
| Moisture Absorption (23°C / 50% RH) | 0.27 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 4.E+00 - 6.E+00 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94V-0 Flame Class Rating (3)(4) | 1.7 | mm | UL 94 by GE |
| Source GMD, last updated:09/30/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 290 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 255 - 265 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 40 - 65 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:09/30/2004 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon DD0009.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|