S-Plastics Stat-kon DD0009XQ resin is a compound based on Polycarbonate containing Carbon Powder and Flame Retardant. Added features
include Electrically Conductive, Flame Retardant and Easy Molding.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break, 5 mm/min | 63 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 11.1 | % | ISO 527 |
| Flexural Stress, break, 2 mm/min | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2800 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 120 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 60°C, flow | 6.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 6.3E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 132 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage, flow | 0.4 - 0.7 | % | S-Plastics Method |
| Density | 1.3 | g/cm³ | ISO 1183 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+04 - 1.E+06 | Ohm | ASTM D 257 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.6 | mm | UL 94 |
| Source GMD, last updated:11/20/2007 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 255 - 290 | °C |
| Front - Zone 3 Temperature | 260 - 270 | °C |
| Middle - Zone 2 Temperature | 255 - 265 | °C |
| Rear - Zone 1 Temperature | 250 - 260 | °C |
| Mold Temperature | 40 - 65 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:11/20/2007 | ||