S-Plastics Ultem EXSM0001 resin isSiltem EXSM0001 is a copolymer providing improved flexibility over standard Ultem resins. The material is designed for wire and cable applications but can also be used for extrusion of profiles and injection molding. Provides Halogen Free (VDE0472) flame retardancy andlow smoke density and toxicity.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 62 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 5 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2410 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 94 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2150 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 0 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 0 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 0 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 0 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 0 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 110 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 0 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 145 | °C | ASTM D 648 |
| Vicat Softening Temp, Rate B/120 | 0 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 0 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.2 | - | ASTM D 792 |
| Melt Flow Rate, 295°C/6.6 kgf | 7 | g/10 min | ASTM D 1238 |
| Density | 0 | g/cm³ | ISO 1183 |
| Matrix Tg | 200 | °C | DMA |
| Halogen Content | 0 | % | S-Plastics Method |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 0 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+16 | Ohm-cm | ASTM D 257 |
| Surface Resistivity | >1.E+15 | Ohm | ASTM D 257 |
| Relative Permittivity, 100 kHz | 3 | - | ASTM D 150 |
| Dissipation Factor, 100 kHz | 0.0061 | - | ASTM D 150 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Oxygen Index (LOI) | 48 | % | ASTM D 2863 |
| Source GMD, last updated:02/27/2007 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 105 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 300 - 320 | °C |
| Nozzle Temperature | 300 - 320 | °C |
| Front - Zone 3 Temperature | 295 - 315 | °C |
| Middle - Zone 2 Temperature | 295 - 315 | °C |
| Rear - Zone 1 Temperature | 295 - 315 | °C |
| Mold Temperature | 65 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 100 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:02/27/2007 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem EXSM0001.pdf |
|