S-Plastics Ultem EXSM0002 resin is Siltem EXSM0002 is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxicity. It is an amber colored transparent material that can be selfcolored and easily processed on conventional equipment.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 43 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 10 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1400 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 48 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1250 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 0 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 0 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 0 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 0 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 0 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 70 | J/m | ASTM D 256 |
| Source GMD, last updated:02/27/2007 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 105 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 300 - 320 | °C |
| Nozzle Temperature | 300 - 320 | °C |
| Front - Zone 3 Temperature | 295 - 315 | °C |
| Middle - Zone 2 Temperature | 295 - 315 | °C |
| Rear - Zone 1 Temperature | 295 - 315 | °C |
| Mold Temperature | 65 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 50 - 100 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:02/27/2007 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem EXSM0002.pdf |
|