S-Plastics Ultem EXUM0183 resin is Developmental glass fiber and mineral filled PEI resin. Providing UL508 compliance through improved CTI. Providing excellent dimension stability and mechanical performance up to high temperatures.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 0 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 126 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 15400 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 192 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 13800 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 0 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 114 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 15000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 167 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 12500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 49 | J/m | ASTM D 256 |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 211 | °C | ASTM D 648 |
| Vicat Softening Temp, Rate B/120 | 0 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 210 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.71 | - | ASTM D 792 |
| Melt Flow Rate, 200°C/3.8 kgf | 0 | g/10 min | ASTM D 1238 |
| Melt Flow Rate, 367°C/6.6 kgf | 6.5 | g/10 min | ASTM D 1238 |
| Density | 1.71 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 220°C/5.0 kg | 0 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:08/08/2007 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 360 - 390 | °C |
| Nozzle Temperature | 360 - 390 | °C |
| Front - Zone 3 Temperature | 360 - 390 | °C |
| Middle - Zone 2 Temperature | 360 - 380 | °C |
| Rear - Zone 1 Temperature | 340 - 380 | °C |
| Mold Temperature | 140 - 160 | °C |
| Back Pressure | 4.5 - 9.5 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Source GMD, last updated:08/08/2007 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem EXUM0183.pdf |
|