S-Plastics Ultem HTX1010F resin is Higher impact, Polyimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 93 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 82 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 40 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3100 | MPa | ASTM D 638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 137 | MPa | ASTM D 790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 3030 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 2082 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 160 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3.2 mm | 1762 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 196 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.26 | - | ASTM D 792 |
| Melt Flow Rate, 337°C/6.6 kgf | 15.5 | g/10 min | ASTM D 1238 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Oxygen Index (LOI) | 39.7 | % | ASTM D 2863 |
| Source GMD, last updated:01/13/2000 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 135 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 10 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 350 - 370 | °C |
| Nozzle Temperature | 350 - 370 | °C |
| Front - Zone 3 Temperature | 350 - 370 | °C |
| Middle - Zone 2 Temperature | 345 - 365 | °C |
| Rear - Zone 1 Temperature | 340 - 360 | °C |
| Mold Temperature | 135 - 165 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:01/13/2000 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem HTX1010F.pdf |
|