S-Plastics Ultem HU1000E resin is Transparent, standard flow Polyimide (Tg 217C) with internal mold release. ECO Conforming. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant.EtO and steam sterilizable.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 110 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 85 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3590 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 173 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3430 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 55 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 38 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 6 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 219 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 207 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 199 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 201 | °C | ASTM D 648 |
| CTE, -40°C to 150°C, flow | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 150°C, xflow | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C to 150°C, flow | 5.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 5.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 211 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 212 | °C | ISO 306 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 188 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.27 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 337°C/6.6 kgf | 12 | g/10 min | ASTM D 1238 |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 1.25 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 17 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:05/04/2007 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 350 - 400 | °C |
| Nozzle Temperature | 345 - 400 | °C |
| Front - Zone 3 Temperature | 345 - 400 | °C |
| Middle - Zone 2 Temperature | 340 - 400 | °C |
| Rear - Zone 1 Temperature | 330 - 400 | °C |
| Mold Temperature | 135 - 165 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:05/04/2007 | ||
|
For more information please download the datasheet |
|
 |