S-Plastics Stat-kon DEL22P resin is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this material
include: Electrically Conductive.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 100 | MPa | ASTM D 638 |
| Tensile Strain, break | 2 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 7900 | MPa | ASTM D 638 |
| Flexural Stress | 152 | MPa | ASTM D 790 |
| Flexural Modulus | 5690 | MPa | ASTM D 790 |
| Tensile Stress, break | 101 | MPa | ISO 527 |
| Tensile Strain, break | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8170 | MPa | ISO 527 |
| Flexural Modulus | 150 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 283 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 74 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 13 | J | ASTM D 3763 |
| Multiaxial Impact | 102 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 34 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 134 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.4E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 7.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 1.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.6E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 143 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.3 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 0.1 | % | ASTM D 570 |
| Mold Shrinkage, flow, 0.75-2.3 mm | 0.1 - 0.3 | % | S-Plastics Method |
| Mold Shrinkage, flow | 0.1 - 0.3 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 0.75-2.3 mm | 0.4 - 0.6 | % | S-Plastics Method |
| Mold Shrinkage, xflow | 0.4 - 0.6 | % | S-Plastics Method |
| Wear Factor Washer | 15 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.55 | - | ASTM D 3702 Modified |
| Static COF | 0.52 | - | ASTM D 3702 Modified |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.18 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+02 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | 1.E+02 - 1.E+06 | Ohm | IEC 60093 |
| Source GMD, last updated:07/05/2006 |
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |
S-Plastics Stat-kon DEL22P.pdf |
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|