S-Plastics Ultem LTX931A resin is Post-industrial recycle based, 30% glass fiber filled, high flow Polyimide blend. ECO Conforming.
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield, 5 mm/min | 115 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 115 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9200 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 190 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8300 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 4 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 150°C, flow | 1.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 5.8E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 188 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 195 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 184 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.52 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.4 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.25 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 19 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:04/28/2004 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 135 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 340 - 360 | °C |
| Nozzle Temperature | 330 - 355 | °C |
| Front - Zone 3 Temperature | 340 - 360 | °C |
| Middle - Zone 2 Temperature | 325 - 350 | °C |
| Rear - Zone 1 Temperature | 315 - 340 | °C |
| Mold Temperature | 135 - 165 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:04/28/2004 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem LTX931A.pdf |
|