S-Plastics Ultem 2400F resin is 40% Glass fiber filled, standard flow Polyimide (Tg 217C). UL94 V0 listing. US FDA and European Food Contact approved. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU2400.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 20 | mg/1000cy | S-Plastics Method |
| Tensile Stress, break, 5 mm/min | 180 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11500 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 240 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10000 | MPa | ISO 178 |
| Hardness, H358/30 | 170 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.33 | W/m-°C | ISO 8302 |
| CTE, 23°C to 150°C, flow | 1.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 4.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 230 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 217 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 225 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.1 - 0.3 | % | S-Plastics Method |
| Density | 1.61 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.8 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.4 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 5 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 35 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3.5 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 3.1 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.0025 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.0019 | - | IEC 60250 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Comparative Tracking Index, M | 100 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 960°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 48 | % | ISO 4589 |
| Source GMD, last updated:10/11/2006 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 370 - 410 | °C |
| Nozzle Temperature | 370 - 410 | °C |
| Front - Zone 3 Temperature | 380 - 420 | °C |
| Middle - Zone 2 Temperature | 370 - 410 | °C |
| Rear - Zone 1 Temperature | 350 - 390 | °C |
| Hopper Temperature | 80 - 100 | °C |
| Mold Temperature | 140 - 180 | °C |
| Source GMD, last updated:10/11/2006 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem 2400F.pdf |
|