S-Plastics Ultem XH6050M resin is Enhanced flow Polyimidesulfone copolymer (Tg 247C) with internal mold release. ECO Conforming, UL94 V0 listing. Resin is subjec to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774).
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 96 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 96 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 6 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 25 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3510 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 158 | MPa | ASTM D 790 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 155 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 3170 | MPa | ASTM D 790 |
| Tensile Stress, yield, 5 mm/min | 95 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 78 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 8.4 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 16.3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3120 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 123 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3070 | MPa | ISO 178 |
| Hardness, H358/30 | 138 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 69 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 74 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 33 | J | ASTM D 3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 196 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 147 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 242 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 217 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 237 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 230 | °C | ASTM D 648 |
| CTE, -40°C to 150°C, flow | 5.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 150°C, xflow | 5.E-05 | 1/°C | ASTM E 831 |
| Thermal Conductivity | 0.22 | W/m-°C | ASTM E 1530 |
| CTE, 23°C to 150°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 242 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 240 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 228 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.3 | - | ASTM D 792 |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.5 - 0.7 | % | S-Plastics Method |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.7 | % | S-Plastics Method |
| Melt Flow Rate, 367°C/6.6 kgf | 12.5 | g/10 min | ASTM D 1238 |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 1.75 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.65 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 8 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Dielectric Strength, in oil, 3.2 mm | 14 | kV/mm | ASTM D 149 |
| Dissipation Factor, 50/60 Hz | 0.018 | - | IEC 60250 |
| Dissipation Factor, 100 Hz | 0.008 | - | IEC 60250 |
| Dissipation Factor, 1 kHz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.007 | - | IEC 60250 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| Glow Wire Flammability Index 960°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature, 3.0 mm | 850 | °C | IEC 60695-2-13 |
| Oxygen Index (LOI) | 45 | % | ISO 4589 |
| Source GMD, last updated:03/30/2004 | |||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 24 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 380 - 405 | °C |
| Nozzle Temperature | 375 - 400 | °C |
| Front - Zone 3 Temperature | 380 - 405 | °C |
| Middle - Zone 2 Temperature | 370 - 395 | °C |
| Rear - Zone 1 Temperature | 360 - 380 | °C |
| Mold Temperature | 135 - 165 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 | mm |
| Source GMD, last updated:03/30/2004 | ||
|
For more information please download the datasheet |
|
 |
S-Plastics Ultem XH6050M.pdf |
|