S-Plastics Stat-kon DX02728Cresin is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material
include: Clean Compounding System.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, break | 99 | MPa | ASTM D 638 |
| Tensile Strain, break | 6.5 | % | ASTM D 638 |
| Flexural Stress | 165 | MPa | ASTM D 790 |
| Flexural Modulus | 5920 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, notched, 23°C | 64 | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 14 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 143 | °C | ASTM D 648 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.24 | g/cm³ | ASTM D 792 |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 4 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 305 - 325 | °C |
| Front - Zone 3 Temperature | 320 - 330 | °C |
| Middle - Zone 2 Temperature | 310 - 320 | °C |
| Rear - Zone 1 Temperature | 295 - 305 | °C |
| Mold Temperature | 80 - 110 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||
Other related products we recommend:
|
For more information please download the datesheet |
|
 |